龙8娱乐国际 packaging silicone

Thixotropic gel ofhigh viscosity forming, can be directly formed lens or asemicircle shape, high temperature not collapse after forming.

2, the product of sapphire, glass and ceramics with excellent adhesion,adhesion on filament support firmly, bond stress lasting;

3, the product after curing, good light transmission performance, anti ultraviolet performance, can be in -60  ~ 250  for outdoor use;

4, excellent thixotropy.

Scope ofapplication: applicable to MCOB and 龙8娱乐国际 filament products such aspackaging

Typical properties:

Ordinal item number value unit

Application

1appearance: A: - white, - white B:

2 viscosity component A (25 ) 45000± 5000 mPa • s

3 viscosity component B (25 ) 3000± 300 mPa • s

4 mixed viscosity (25 ) micro white colloid

Aftercuring

5 hardness (25 ) 50± 5 shore A

Instructionsfor use:

1, A, B glue in the weight ratio of 1:1 after mixing, packed in glass bottles, such as in the mixing process in theair, should be before the adhesive to the filament and the material, use vacuum to completely extract.

2, the substrate in the glue shouldbe thoroughly cleaned and dried to removeimpurities, water, oil, dustetc..

3, curing conditions: 100  drying for 1 hours (must be exhausted before thebubble drying), 150  oven for 3 hours.

4, 龙8娱乐国际 filament after curing, not prereflow should be sea龙8娱乐国际 or vacuum packaging preservation, to prevent moisture absorption.

5, A, Bglue mixture must be finished within 6 hours.

Note: some of the materials, chemical agent, curing agent and plasticizer can inhibit the elastomer cured. The mostnotable include:

1, organic tin and other metal organic compounds

2, sulfur, polysulfide, polysulfones or othersulfur-containing items

3, amine, polyurethane rubber or ammoniacontaining items

4, phosphorus or phosphoruscontaining items

5, some fluxresidue

If in doubt whether can inhibit the curing of a certain material or material, we recommend a compatibility experiments to test the suitability for a particularapplication. If the existence of packaging material of uncured elastomer material interface between the substrate and the cured doubt, thatincompatible, will inhibit the curing.

Packing: 1, glass or plastic bottles packaging, specifications have 1kg, group 2kg/, group 4kg/ packaging.

2, indicated on the package name, brand name, batch number, weight,manufacturer, production date.

Save: 1, thisproduct should be below 25 , avoid light and closed storage.

2, the product storage period is 6 months from the date of manufacture.

Statement: all data contained herein are for reference only, and is believed to be reliable, for any one approachis adopted to get beyond ourcontrol results,we will not be responsible for each user, suggested in theofficial use of the former shouldbe based on data provided by the first test.

 