Home > Renderings > Special silk printing silica QK-3013 A&B

Special silk printing silica QK-3013 A&B

SiliconeQK-3013

First, the characteristics of the product


Silicon QK-3013 is transparent two-component, high strength, high transparency, high tear resistance, soft hand feeling, strong adhesion, small shrinkage rate, operational time up to 20 hours of new siliconelabel rubber;new material used in Japan advanced technology (is currently widely used in the three-dimensional trademark printing, clothing. Printer ribbon, silk screenprinting, quality products). For verycomplex shape and high precision model.

Two, property

high transparent;

 small shrinkage;

 two method:

(1), the standard type (2), themachine mixing

 if making speed to control or slow down to thedeployment of curing agentamount;

 if making speed to control or slow down to thedeployment of curing agentamount;

Three, application

 suitable for cloth standard, anti-counterfeit trademarks and silkscreenprinting silica gel;

 suitable forenvironmental protection brandtrademark, stereoscopic trademark;

Controldevice, more suitable for automobile industry heating device,decorative lights, etc..

Four, technical indicators

Solids content

 %

 100

 Mixed viscosity

 mPa.s

 35,000

 As molded
 D7921

 Specific gravity

 1.09

 D2241

 Hardness

 Shore A

 33

 D4112 DIE C

 Tensile strength

 MPa (psi)

 4.5 (725)

 D4112 DIE C

 Elongation at break

 %

 400

 D6214 DIE B

 Tear strength

Volume resistivity

 kN/m (Ppi)

Ohm.cm

 5(40)

4.5xl0l5

 

The A, B agent 10:1 by weight are mixed uniformly, and vacuum exhaustbubble.

The curing time and temperature: 205 ° C/15-40 seconds (for reference only,please consider the actual operation.).

 operating time is 20 hours.

Six, packaging

The product packaging for 20kg/.

Direction for use :

Use ratio of A and B = now, before the use should be A, B component in proportion to fully mix evenly, quiet place TuoPao or vacuum TuoPao.

Don't touch the containing N, P, S plasma compounds and contain alkynyl and vinyl compounds, lest make, platinum catalyst poisoning and cannot cure, especially PVC contains Pb (lead), can make the catalyst poisoning some organic pigments can also lead to curing slowed or not curing.

 

 

CopyRight© QKing Technology Record Number:粤ICP备09040588号 Website Legal Counsel: Huang Yuan lawyers Address: Pinghu, Longgang District, Shenzhen, Guangdong, South China International Industrial City Hardware M14 chemical District Building
You are this sitevisitors